Mn13 X120Mn12 Mn12 High Manganese Wear-resistant Steel pdf
High manganese austenitic steel such as Mn13 and X120Mn12, Mn12 have good toughness and remarkable surface work hardening properties. Under strong impact load or extrusion load, he stressed surface is work hardened, and the surface hardnes can be significantly increased from the initial HB200 to over HB750, while the core ofsteel plate still maintains good impact toughness, it is widely used in mining equipment, machinery manufacturing industry, such as shot blasting equipment, large-scale iavcrusher, etc.
Quenched X120Mn12 manganese steel plate, also referred to as manganese hard steel or hard manganese steel plate, features a unique material property: intense cold working can substantially raise the hardness and tensile strength of its cold-worked surface layer, while causing no negative impact on the material's inherently excellent toughness. Cold working treatment greatly improves the wear resistance of G-X120MN12 steel plates. Thanks to superior toughness, X120Mn12 grade manganese steel plates support multiple processing methods, including flanging, bending and piercing.
X120Mn12 high manganese steel plates have extensive application value across multiple industries and general scenarios. Typical finished products and components cover crusher jaws, power shovel bolts, impact mills, centrifugal mills, protective grilles, security doors, crusher jaw inserts, power shovel connectors, gripping teeth, cladding panels and safety plates.
This type of steel plate adapts well to impact stress and heavy percussion working environments. It is widely utilized as wear-resistant plates for stone and iron chutes, industrial track structures and engineering construction machinery. Meanwhile, the material is also applicable for anti-drill plates used in shot blasting equipment, tumbling machines, safety doors and a wide range of other industrial facilities.
Mn13 X120Mn12 Mn12 High Manganese Wear-resistant Steel Product Performance and Available Specification From GNEE
Shot blasting equipment madeof high-manganese austenitic wear-resistant steel Mn13
Mining machine made of high-manganese austenitic wear-resistant steel Mn13
What is X120Mn12 material?
austenitic hard manganese steel
1.3401 X120Mn12 is an austenitic hard manganese steel. Work hardening of the surface under mechanical stress greatly increases the wear resistance and surface hardnesses of up to 500 HB are achieved, while the core remains tough. Components with high mechanical impact and shock loads.
What is Mn13?
Mn13 is a high-manganese steel with approximately 12-14% manganese and the remainder iron. Typically available as plates or sheets, it is also an abrasion-resistant steel known for excellent wear resistance and impact toughness. Mn13 is used in mining, heavy machinery, construction equipment, and material handling. It is often used as-rolled but can be further processed through heat treatment or machining.
Mn13 Steel Plate Applications
Mn13 high-manganese wear-resistant steel is primarily used in shot blasting machines, ball mill liners, crushers, and power plant fan blades. Mn13 boasts a highly wear-resistant surface layer and excellent impact toughness. Many new materials and modern surface engineering technologies still cannot match the cost-effectiveness of high-manganese steel.
What is Mn13 steel equivalent to?
Mn13 is similar to ASTM A128 Grade A and is also called Hadfield steel. Its ideal for mining and heavy machinery applications.
What is equivalent to X120MN12 steel?
The list of equivalents and other designations of X120Mn12: 110G12, 11 G 12, 110 G 12, X120MN12, X 120 MN 12, 1.3401, 3401, 120 MN 12, HADFIELD, X110MN14, X 110 MN 14, 1.3402, 3402, L120G13, 110G13L, 110Г13Л, G13, Г13, 120G13.
What is the heat treatment of X120Mn12?
Heat treatment and structure of X120Mn12
To give the characteristic properties to Hadfield steel, the product is subjected to supersaturation at a temperature of 950-1000 ℃ and cooled in water, which gives us austenitic material structure. After this treatment, the steel is difficult to process.
What is 1.3401 steel number?
Din 1.3401, Manganese Steel. Manganese can reach a hardness score of almost 600 BHN, giving it about 5 times the hardness of mild steel, and almost 3 times the hardness of annealed stainless steel. High Manganese (Manganal) is an austenitic (nonmagnetic), work-hardening steel.
X120Mn12, 1.3401 - purpose
steel baskets and buckets of excavators
steel for jaws for stone breakers
steel for prison bars and safes
steel for covers and construction parts of electromagnets
steel for molds for pressing briquettes
steel on tracks, pins, shafts and bushings of track chains
steel for baskets of excavators and tractors
steel for turnouts and railway and tram crossing
steel and cast steel for ball mills
steel for walls of storage bunkers served by electromagnets in the form of sheets
wear-resistant steel for wire sieves
steel for conveyors and pipelines for the pneumatic transport of crushed and ground materials