What is S890QL steel plate?
S890QL is a structural steel grade with an even greater yield strength than S690QL. The material serves as a great option for procurers who wish to promote high strength in a cost effective way. Due to the characteristics of the steel, clients can use this material in numerous applications resulting in a leaner build whilst still maintaining great strength.
S890QL is a water quenched & tempered steel which complies with the EN10025:6:2004 specification.
Please refer to the technical details below referring to S890QL.
Grade Designation
- S = Structural Steel
- 890 = minimum yield strength (MPa)
- Q = Quenching & Tempering
- L = Low notch toughness testing temperature
Chemical Composition of S890QL
| % | |
|---|---|
| C | 0.20 |
| Si | 0.80 |
| Mn | 1.70 |
| P | 0.020 |
| S | 0.010 |
| N | 0.015 |
| B | 0.0050 |
| Cr | 1.50 |
| Cu | 0.50 |
| Mo | 0.70 |
| Nb | 0.06 |
| Ni | 2.0 |
| Ti | 0.05 |
| V | 0.12 |
| Zr | 0.15 |
Mechanical Properties of S890QL
| Designation | Mechanical Properties (ambient temperature) | |||||||
|---|---|---|---|---|---|---|---|---|
| Steel Name | Steel Number | Min. Yield Strength ReH MPa | Tensile Strength Rm MPa | Min. & elongation after fracture | ||||
| Nominal thickness (mm) | Nominal thickness (mm) | |||||||
| >3 <50 | >50 <100 | >100 <150 | >3 <50 | >50 <100 | >100 <150 | |||
| S890QL | 1.8983 | 890 | 830 | -- | 940/1100 | 880/1100 | -- | 11 |
V Notch Impact Testing
| Grade | Sample Orientation | @ 0 Deg C | @ -20 Deg C | @ -40 Deg C | @ -60 Deg C |
|---|---|---|---|---|---|
| S890QL | Longitudinal | 50J | 40J | 30J | |
| Transverse | 35J | 30J | 27J |
Characteristics of S890QL Structural Steel Plates ?
1.Mammoth Strength
Suppliers of AFNOR E890TFP High Tensile plates, ranking high in overall tenacity and impact-bearing strength. S890QL series includes High Yield Steel Plates made from combinations like Carbon-Steel, Carbon-Manganese Steel, High strength-low alloy Steel, High strength, tempered and quenched Low Alloy Steel, etc. The alloying agents bolster humungous vigour in each plate, harnessing maximum profit. Consequently, taut Steel plates easily endure mighty impact collisions, standing strong in rain, storm and sun.
2. Accelerate Construction Speed
Unlike cement, which ultimately requires a few weeks to set after being poured, NF A36-204 S890T Steel Plates can be used as soon as they are conveyed to the construction site. The Steel plates can be quickly fabricated, catalyzing the speed of construction.
3. Beneficial in High-Stress Industries
No compromise on quality makes us the leading stockists of ISO4952 E890 High-Strength Quenched and Tempered Steel Plates, ready to take on the world. Manufactured from the purest Steel combined with alloys enable, S890QL Steel plates have a lighter body weight, creating equally light superstructures and benefitting constant machining in severe applications.
4. Ductile and Versatile
Their colossal frames, JFE HITEN 780LE High Strength Plates, are malleable without being fragile. Such Steel can display up to four times the power of ordinary structural Steel, directing low steel usage, and cost-saving for contractors and clients. Similarly, its elasticity aids architects in building exquisitely multipurpose, aesthetic and grand structures.
Email: info@gneesteels.com
Whatsapp (WeChat) :+86 15824687445
| Other steel plate | ||||
| Name | Material | Specification (mm) | Tons | Remark |
| Low Alloy | Q345A, Q345B, Q345C, Q345D, Q345E, Q390, Q420, Q460C, ST52-3, S355J2+N, SS400, SA302GrC, S275NL, 35CrMo | 6 - 350 | 5788.56 | Normalizing, tempered ,controlled rolling, hot rolling , Hot rolling,1st inspection, 2nd inspection, 3rd inspection |
| Pressure Vessel Plate | Q245R, Q345R, Q370R, 16MnDR, 09MnNiDR, 15CrMoR, 14Cr1MoR, 12Cr2Mo1R, SA516Gr60, SA516Gr70, SA516Gr485, SA285, SA387Gr11, SA387Gr12, SA387Gr22, P265,P295,P355GH,Q245R(R-HIC),Q345R(R-HIC) | 3 - 300 | 8650 | Normalizing, tempered ,controlled rolling, hot rolling , Hot rolling,1st inspection, 2nd inspection, 3rd inspection |
| High-Strength Plate | WH785D/E,Q960D/E, Q890D/E,WH60D/E,WH70B,Q550D,Q590D,Q690D/E | 8 - 120 | 3086.352 | Quenched and tempered |
| Wear-Resistant Plate | NM360, NM400, NM450, NM500 | 6 - 150 | 3866.297 | Quenched and tempered |
| Bridge Plate | Q235qC, Q345qC, Q370qC, Q420qC, Q345qDNH, Q370qDNH, A709 - 50F - 2, A709 - 50T - 2 | 8 - 200 | 2853.621 | Hot rolling, normalized ,hot rolling controlled rolling, quenched and tempered + toughness and brittleness |